| ltem | Method A | Method B |
| Test temperature | 75±2"C | 75+2°℃ |
| Speed of spindle | 1200+60 r/min | 1200+60 r/min |
| Testing time | 60±1min | 60±1min |
| Axial testing force | 147N(15kgf) | 392N(40kgf) |
| Axial testing force zero point inductance | ±1.96N(±0.2kgf) | ±1.96N(o.2kgf) |
| Standard steel-ball specimen | 12.7mm | 12.7mm |
| Name | rubber wear resistance akron abrasion testing machine |
| Grinding wheel size | Diameter of 150mm, the thickness of 25m, center hole diameter of 32mm; particle size of 36,abrasive alumina |
| Sand wheel | D150mm,W25mm, particle size 36 # combine |
| Specimen size Note: D for rubber tire diameter, h is the thickness of the sample | Strip [length (D+2 h)of+0~5mm,12.7±0.2mm; thickness of 3.2mm,±0.2mm] Rubber Wheel diameter 68 °-1mm, thickness of 12.7±0.2mm, hardness of 75 to 80 degrees |
| Specimen tilt angle range | " to 35 ° adjustable |
| Weight weight | Each of 2lb,6Lb |
| Transfer speed | BS250±5r/min;GB76±2r/min |
| Counter | 6-digit |
| Motor specifications | 1/4HP[O.18KW) |
| Size of the machine | 65cmx50cmx40cm |
| The weight of the machine | 6Okg |
| Balance hammer | 2.5Kg |
| Counter | |
| Power Supply | single phase AC 220V 3A |
3-2 Make sure the right test standard is chosen
4 Defining Specimen:
Click on the new specimen button
5- Define a name for the specimen and put the number of specimens in the blank and select OK:
6- Click on Batch modify button to put the specification and all the required information and click OK:
7- Modify the information on the main screen if needed:
8- The samples must be conditioned according to the test standard.
9- Put the sample in the grips and make sure it is positioned in the middle of the grips.
The upper jaw can move using the up and down buttons:
10- For starting the test you need to click the Test button:
11- The live test result can be seen through the tabs:
This is a Multi graph result sample: