Diameter of 150mm, the thickness of 25m, center hole diameter of 32mm; particle size of 36,abrasive alumina
Sand wheel
D150mm,W25mm, particle size 36 # combine
Specimen size Note: D for rubber tire diameter, h is the thickness of the sample
Strip [length (D+2 h)of+0~5mm,12.7±0.2mm; thickness of 3.2mm,±0.2mm] Rubber Wheel diameter 68 °-1mm, thickness of 12.7±0.2mm, hardness of 75 to 80 degrees
Specimen tilt angle range
" to 35 ° adjustable
Weight weight
Each of 2lb,6Lb
Transfer speed
BS250±5r/min;GB76±2r/min
Counter
6-digit
Motor specifications
1/4HP[O.18KW)
Size of the machine
65cmx50cmx40cm
The weight of the machine
6Okg
Balance hammer
2.5Kg
Counter
Power Supply
single phase AC 220V 3A
It consists of a test chamber, a runner, a sample holder and a control panel. When conducting the test, the rubber sample is placed on the stand, and the test conditions such as load and speed are set on the control panel. The specimen holder is then rotated against the grinding wheel for a specified period of time. At the end of the test, the degree of wear is calculated by measuring the weight loss of the specimen or the depth of the wear track. Test results obtained from the Rubber Abrasion Resistance Akron Abrasion Tester are used to determine the abrasion resistance of rubber articles such as tires, conveyor belts, and shoe soles. Applicable industries: rubber industry, shoe industry. Determination of standard: GB/T1689-1998vulcanized rubber wear resistance machine(Akron)